GH-110
Flexible Graphite Packing (NA) Construction:
This packing
is manufactured from high purity flexible graphite that is
expanded and formed into a braidable yarn and then braided
without binders or wire reinforcement. It also contains corrosion
inhibitor to prevent the electrical-chemical reaction. The
finished product retains all the inherent benefits of flexible
graphite: heat resistance, chemical inertness, low friction,
self lubrication, and conforms readily.
Application:
The
outstanding properties of GH-110 make it a truly multi-service
packing capable of a wide variety of uses throughout a plant.
It may be used in valves, pumps, expansion joints, mixers
and agitators in the hostile environments of hydrocarbon processing,
pulp and paper, power generation, metal-working and other
industries where effective sealing is vital. |
| Service
Limits: |
|
|
 |
 |
 |
| Pressure (Bar) |
30 |
300 |
500 |
| Temperature |
-250~450
(In Oxidizing Atmosphere)
-250~650
(In Steam)
-250~1650
(In Non-Oxidizing Atmosphere) |
| Shaft Speed (m/s) |
0~20 |
| PH Range |
0~14
(except strong oxidizers) |
|
|
Main
Properties of GH-110 Flexible Graphite Packing: |
| Item |
Unit |
Value |
|
Dimensional deviation |
mm |
axial
0.00mm~+0.50mm |
| radial
0.00mm~-0.50mm |
| Carbon Content |
In Graphite |
% |
＞99
|
| In Packing |
＞90 |
| Density |
g/cm3 |
0.9~1.3 |
|
Compressibility |
% |
25~50 |
| Resilient |
% |
＞15 |
| Ignition Loss |
% |
＜10 (450, 3hours) |
|
Friction factor |
|
＜0.2 |
| Total
sulphur |
ppm |
＜1500 |
| Total
chlorine |
ppm |
＜50 |
| Total
metal |
ppm |
＜500 |
| Total
fluorine |
ppm |
＜20 |
|
|
Specifications: |
| Style |
Reinforced Material |
| 110C-1 |
Cotton Fiber |
| 110C-2 |
Cotton Fiber + Inconel |
| 110C-3 |
Cotton Fiber + Stainless Steel Wire |
| 110G-1 |
Fiberglass |
| 110G-2 |
Fiberglass + Inconel |
| 110G-3 |
Fiberglass + Stainless Steel Wire |
| 110K |
Cotton Fiber + Kevlar(Aramid) Fiber |
| 110T |
Cotton Fiber + Carbon Fiber |
|
|
 |
GH-1108
Valve Stem Packing (NA) Construction:
The packing
is manufactured from high purity flexible graphite that is
expanded and formed into a weave-able yarn and then braided
in a unique construction with wire reinforcement. It also
contains corrosion inhibitor to prevent the electrical-chemical
reaction. The finished product retains all the inherent benefits
of flexible graphite; while the wire reinforcement provides
greater mechanical strength.
Application: This packing
is particularly suited for use in high temperature, high pressure
steam service. In addition, it can also handle most chemicals,
acids and alkalis. It is excellent for use in steam turbines,
high temperature motor-actuated valves and for high pressure/high
temperature valve applications in general.
|
|
 |
| Service
Limits: |
|
|
|
|
|
| Pressure (Bar) |
-- |
-- |
600 |
| Temperature |
-250~450
(In Oxidizing Atmosphere)
-250~650
(In Steam)
-250~1650
(In Non-Oxidizing Atmosphere) |
| Shaft Speed (m/s) |
--- |
| PH Range |
0~14
(except strong oxidizers) |
|
|
| 
|
GH-1900
Valve Stem Packing (NA)
Construction:
his
packing is braided over the core of GH-1108 packing,
using high temperature fiber reinforced with Inconel wire braided
the jacket, then coated with graphite and corrosion inhibitor.
Result is a dense, long-lived, non-hardening packing, is readily
die-formed and is easily removed. It also contains corrosion
inhibitor to prevent the electrical-chemical reaction.
Application: The packing
is especially designed for super-critical fossil fuel power
plants and for all ranges of steam valves. Excellent on valves
of steam turbines; automatic tube blowers; high temperature,
motor-actuated slide valves; and on all general high pressure
valving.
|
| Service
Limits: |
| |
|
|
|
| Pressure (Bar) |
-- |
-- |
400 |
| Temperature |
-200~650 |
| Shaft Speed (m/s) |
-- |
| PH Range |
2~12 |
|
|
|